Incoming Inspection | → | Mixing | → | Melting | → | Powder | → | Pressing |
↓ | ||||||||
Packing and Delivery | ← | Final Inspection | ← | Shape Processing | ← | Magnetic Testing | ← | Sintering |
Incoming Inspection | → | Mixing | → | Melting | → | Powder | → | Pressing |
↓ | ||||||||
Packing and Delivery | ← | Final Inspection | ← | Shape Processing | ← | Magnetic Testing | ← | Sintering |
Characteristic physical properties of sintered NdFeB magnet material at 20°C<o:p> | ||
Density<o:p> | 7.6<o:p> | g/cm3<o:p> |
Vickers hardness<o:p> | 600<o:p> | HV<o:p> |
Flexural strength<o:p> | 240<o:p> | MPa<o:p> |
Tensile strength<o:p> | 75<o:p> | MPa<o:p> |
Young's modulus<o:p> | 150000<o:p> | MPa<o:p> |
Curie temperature<o:p> | 310<o:p> | °C<o:p> |
Specific electrical resistivity<o:p> | 1.2...1.6<o:p> | µΩm<o:p> |
Specific heat<o:p> | 450<o:p> | J/(kg.K)<o:p> |
Thermal conductivity<o:p> | 8...9<o:p> | W/(m.K)<o:p> |
Coefficient of thermal expansion parallel to magnetization direction<o:p> | 5...7<o:p> | 10-6/K<o:p> |
Coefficient of thermal expansion perpendicular to magnetization direction<o:p> | -3...-1<o:p> | 10-6/K<o:p> |
Welcome to contact us ,we are 24 hours on line,Ms Wu is at your service:
Cell phone:86+13855156049 86+18009691660
Skype:rainbow0051
We will reply your email or fax within 24 hours.
Characteristic physical properties of sintered NdFeB magnet material at 20°C<o:p> | ||
Density<o:p> | 7.6<o:p> | g/cm3<o:p> |
Vickers hardness<o:p> | 600<o:p> | HV<o:p> |
Flexural strength<o:p> | 240<o:p> | MPa<o:p> |
Tensile strength<o:p> | 75<o:p> | MPa<o:p> |
Young's modulus<o:p> | 150000<o:p> | MPa<o:p> |
Curie temperature<o:p> | 310<o:p> | °C<o:p> |
Specific electrical resistivity<o:p> | 1.2...1.6<o:p> | µΩm<o:p> |
Specific heat<o:p> | 450<o:p> | J/(kg.K)<o:p> |
Thermal conductivity<o:p> | 8...9<o:p> | W/(m.K)<o:p> |
Coefficient of thermal expansion parallel to magnetization direction<o:p> | 5...7<o:p> | 10-6/K<o:p> |
Coefficient of thermal expansion perpendicular to magnetization direction<o:p> | -3...-1<o:p> | 10-6/K<o:p> |