Quantity: | |
---|---|
Piece/Arc magnet manufacturer
1 Arc magnet manufacturer
Sintered Hard Arc magnet manufacturer
1.Shape
Arc
2:Size
Customized size per your requirements.
Tolerance:+/-0.05mm, +/-0.1mm or per your request
Shape | max.size | min.size |
Block | 240*100*40 | 2*2*1 |
Cylinder | D240*40 | D2*1 |
Ring | OD240*40 (hole size customized) | D5*1*1 |
Arc | per your request | |
And other special shape magnet per your request |
3.Grade
N35-N52, N35M-N50M, N35H-N48H, N35SH-N45SH, N28UH-N42UH,
N28EH-N40EH, N28AH-N38AH.
4.Coating
Ni, Ni-Cu-Ni, Zn(Cr3+), Tin, Epoxy, Ni-Ag, Ni-Au, Passivation, Parylene, etc.
5.Production Time
We have materials in stock and continuous produce,about 7-10days
6.Applications
Motors, Generators, Sensors, Speakers, Earphones and other musical instruments,
Magnetic therapy devices, Magnetic Chuck, Magnetic bearings and couplings,
NdFeB Pot Magnet and other magnetic applicatications
Sintered Hard Arc magnet manufacturer
1.Shape
Arc
2:Size
Customized size per your requirements.
Tolerance:+/-0.05mm, +/-0.1mm or per your request
Shape | max.size | min.size |
Block | 240*100*40 | 2*2*1 |
Cylinder | D240*40 | D2*1 |
Ring | OD240*40 (hole size customized) | D5*1*1 |
Arc | per your request | |
And other special shape magnet per your request |
3.Grade
N35-N52, N35M-N50M, N35H-N48H, N35SH-N45SH, N28UH-N42UH,
N28EH-N40EH, N28AH-N38AH.
4.Coating
Ni, Ni-Cu-Ni, Zn(Cr3+), Tin, Epoxy, Ni-Ag, Ni-Au, Passivation, Parylene, etc.
5.Production Time
We have materials in stock and continuous produce,about 7-10days
6.Applications
Motors, Generators, Sensors, Speakers, Earphones and other musical instruments,
Magnetic therapy devices, Magnetic Chuck, Magnetic bearings and couplings,
NdFeB Pot Magnet and other magnetic applicatications
Curie Temp. | Tc | °C | 800-850 | Coeff. Of thermal expansion | C // | 1/°C | ~8×10-5 |
Density | D | g/cm3 | 8.3-8.5 | C⊥ | 1/°C | ~11×10-5 | |
Recoil permeability | rec | 1.00-1.05 | Regidity Strength | N/m2 | ~1.5×108 | ||
Max.working Temp. | Tmax | °C | 350 | Compress Strength | N/m2 | ~8×108 | |
Electrical Resistivity | ΩCm | ~8.6×10-5 | Tensile Strength | N/m2 | ~3.5×107 | ||
Vickers Hardness | Hv | 500-600 | Young’s modulus | N/m2 | ~1.2×1011 | ||
Thermal Conduct Rate | W/mK | ~12 | Magnetization field Ha | kA/m | ≥1600 |
Curie Temp. | Tc | °C | 800-850 | Coeff. Of thermal expansion | C // | 1/°C | ~8×10-5 |
Density | D | g/cm3 | 8.3-8.5 | C⊥ | 1/°C | ~11×10-5 | |
Recoil permeability | rec | 1.00-1.05 | Regidity Strength | N/m2 | ~1.5×108 | ||
Max.working Temp. | Tmax | °C | 350 | Compress Strength | N/m2 | ~8×108 | |
Electrical Resistivity | ΩCm | ~8.6×10-5 | Tensile Strength | N/m2 | ~3.5×107 | ||
Vickers Hardness | Hv | 500-600 | Young’s modulus | N/m2 | ~1.2×1011 | ||
Thermal Conduct Rate | W/mK | ~12 | Magnetization field Ha | kA/m | ≥1600 |